Epitaxial strain and thickness dependent structural, electrical and magnetic properties of La0.67Sr0.33MnO3 films

Résumé

The crystal structural quality and the strain induced by the substrate strictly impose the magnetic and transport properties of La0.67Sr0.33MnO3 (LSMO) films. In particular, the magnetic anisotropy (MA) of epitaxial LSMO can be finely tuned by varying its thickness and by choosing single crystal substrates with suitable lattice mismatch with the film. Here, we have deposited LSMO films with thicknesses in the 12-50 nm range by pulsed laser deposition on different single crystal substrates inducing either compressive or tensile in-plane strain on the manganites. The epitaxial quality of films was quantified by ω-scans around (002) peak with full-width half-maximum (FWHM) values as low as 0.08° for films on the nearly matched NGO (110) substrate to 1.4° films on high mismatched MgO (001) substrate. As the epitaxial strain in thin-film increases, a significant reduction in metal-insulation transition (MIT) temperature (Tp) was observed. The magnetic properties of the films probed by Kerr magnetometry show that the symmetry of the room temperature MA varies significantly as a function of both strain and thickness. Specifically, we observed pure uniaxial MA on NGO (110) and pure biaxial MA on STO buffered MgO (001), whereas a spin reorientation from uniaxial in-plane to out-of-plane on LSAT (001) and uniaxial to nearly isotropic in-plane on STO (001) substrate as the film thickness is increased. We provide an efficient tool to tune the MA according to the specific spintronic application targeted.
Fichier principal
Vignette du fichier
2020_J._Phys._D__Appl._Phys._10.1088_1361-6463_accepted_manuscript_Chaluvadi.pdf (1.04 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02568880 , version 1 (10-05-2020)

Identifiants

Citer

Sandeep Kumar Chaluvadi, Fernando Ajejas, Pasquale Orgiani, Sylvain Lebargy, Albert Minj, et al.. Epitaxial strain and thickness dependent structural, electrical and magnetic properties of La0.67Sr0.33MnO3 films. Journal of Physics D: Applied Physics, 2020, 53, pp.375005. ⟨10.1088/1361-6463/ab8e7b⟩. ⟨hal-02568880⟩
48 Consultations
286 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More